Anti reflective coating polymers and the preparation method thereof

ABSTRACT

The present invention relates to organic anti-reflective coating polymers and preparation methods therefor. Anti-reflective coatings are used in a semiconductor device during photolithography processes to prevent the reflection of light from lower layers of the device, or resulting from changes in the thickness of the photoresist layer, and to eliminate the standing wave effect when ArF light is used. The present invention also relates to anti-reflective compositions and coatings containing these organic anti-reflective coating polymers, alone or in combination with certain light-absorbing compounds, and preparation methods therefor. When the polymers of the present invention are used in an anti-reflective coating in a photolithography process for forming submicro-patterns, the resultant elimination of changes in CD due to diffractive and reflective lights originating from lower layers increases the product yield in the formation of submicro-patterns during the manufacture of 64 M, 256 M, 1 G, 4 G and 16 G DRAM semiconductor devices.

This application is a divisional of Ser. No. 09/413,679 filed Oct. 7,1999, now U.S. Pat. No. 6,350,818.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to organic polymers suitable for use inanti-reflective coatings on semiconductor devices, and methods forpreparing them. More specifically, the polymers of the present inventioncan be used to form a layer which prevents the reflection of light fromlower layers coated on a semiconductor chip when photolithographyprocesses using short wavelength light sources, such as 248 nm (KrF) and193 nm (ArF) wavelengths, are employed during the manufacture of 64M,256M, 1G, 4 G and 16 G DRAM semiconductor devices. Anti-reflectivecoatings comprising polymers of the present invention also eliminate thestanding wave effect when an ArF beam is used, andreflection/diffraction caused by changes in the thickness of thephotoresist layer itself. The present invention also relates to ananti-reflective composition containing these polymers, alone or incombination with other light-absorbing compounds, and the anti-reflective coating formed from these compositions, as well aspreparation methods therefor.

2. Description of the Prior Art

In photolithography processes for forming submicro-patterns during themanufacture of semiconductors, it is unavoidable to have reflectivenotching of the standing wave of the exposing radiation. This effect isdue to the spectroscopic properties of the lower layers coated on thesemiconductor wafer, changes in the photoresist layer and variations inthe critical dimension (CD) due to diffracted and reflected light fromthe lower layer. Therefore, it has been suggested that a layer, calledan anti-reflective coating, be introduced into the semiconductor deviceto prevent the reflection of light from the lower layers. Thisanti-reflective coating usually comprises an organic material thatabsorbs light in the wavelength range of the light beam source used inthe lithography process.

Anti-reflective coatings are categorized into inorganic and organicanti-reflective coatings depending on the coating materials used, orinto light-absorbing and light-interfering coatings depending on themechanism.

An inorganic anti-reflective coating is used mainly in the process ofsubmicro-pattern formation using i-line radiation with a wavelength of365 nm. TiN and amorphous carbon have been widely used inlight-absorbing coatings, and SiON has been used in light-interferingcoatings.

Inorganic SiON has been used for anti-reflective coatings insubmicro-pattern formation processes using a KrF beam. A recent trendhas been to try to use organic compounds in an anti-reflective coating.Based on knowledge to date, the following are prerequisites for anadequate organic anti-reflective coating:

First, during the pattern formation process, the photoresist must not bepeeled from the substrate by dissolving in the solvent used in theorganic anti-reflective coating. For this reason, the organicanti-reflective coating needs to be designed to form a cross-linkedstructure, and must not produce chemicals as a by-product.

Second, acid or amine compounds must not migrate in or out of theanti-reflective coating. This is because there is a tendency for“undercutting” at the lower side of the pattern if an acid migrates, andfor “footing” if a base such as an amine migrates.

Third, the anti-reflective coating must have a faster etching speedcompared to the photoresist layer so that the etching process can beperformed efficiently by utilizing the photoresist layer as a mask.

Fourth, the anti-reflective coating must function with a minimalthickness.

Up to now, suitable anti-reflective coatings have not been developed.for use in processes for forming a submicro-pattern using an ArF beam.Furthermore, since there is no known inorganic anti-reflective coatingwhich controls the interference from a 193 nm light source, the use oforganic chemicals in anti-reflective coatings is currently beingstudied.

Therefore, it is desirable to use and develop organic anti-reflectivecoatings that absorb light strongly at specific wavelengths to preventthe standing wave effect and light reflection in lithography processes,and to eliminate the rear diffraction and reflected light from the lowerlayers.

SUMMARY OF THE INVENTION

The present invention provides novel chemical compounds suitable for usein anti-reflective coatings in photolithography processes for formingsubmicro-patterns using 193 nm (Arf) and 248 nm (KrF) light beams in themanufacture of semiconductor devices.

The present invention further provides preparation methods for chemicalcompounds to be used in anti-reflective coatings.

The present invention also provides anti-reflective coating compositionscontaining the above-mentioned compounds and preparation methodsthereof.

The present invention also provides anti-reflective coatings formed byusing the above-mentioned anti-reflective composition, and methods forthe formation thereof.

DETAILED DESCRIPTION OF THE INVENTION

Polymers of the present invention are selected from the group consistingof compounds represented by the following general formulas (1), (2) and(3):

wherein, R is hydrogen, a C₁-C₆ alkyl group, hydroxy or hydroxymethyl;and m:n is the mole ratio of 0.1-0.9:0.1-0.9;

wherein, R is hydrogen, a C₁-C₆ alkyl group, hyrdoxy or hydroxymethyl; xis an number between 1 and 5; and a:b:c:d is the mole ratio of0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9; and

wherein,

R₁ is hydrogen, methyl or hydroxy; and e is the average degree ofpolymerization. Preferably e has a value of 3.0˜17.0.

The polymers of the present invention are designed to facilitate lightabsorption at wavelengths of 193 nm and 248 nm by having groups thatabsorbs light strongly at both wavelengths;

The polymers represented by general formula 1 above can be prepared inaccordance with the reaction equation i set forth below, whereinpolyhydroxystyrene resin (Compound I) and diazonaphthoquinone halide(Compound II) are reacted in a solvent in the presence of an amine:

wherein, R is hydrogen, a C₁-C₆ alkyl group, hydroxy or hydroxymethyl; Yis a halogen group; and m:n is the mole ratio of 0.1-0.9:0.1-0.9.

The polymer represented by the general formula 2 above can be preparedin accordance with reaction equation 2 set forth below, whereinpoly(styrene-acrylate) resin (Compound III) and diazonaphthoquinonehalide (Compound II) are reacted in a solvent in the presence of anamine:

wherein, R is hydrogen, a C₁-C₆ alkyl group, hydroxy or hydroxymethyl; Yis a halogen group; x is an number from 1 to 5; and a:b:c:d is the moleratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9.

The polymer represented by general formula 3 above can be prepared inaccordance with reaction equation 3 set forth below, wherein novolacresin (Compound IV) and diazonaphthoquinone halide (Compound II) arereacted in a solvent in the presence of an amine:

wherein, R₁ is hydrogen, methyl or hydroxy; Y is a halogen group; and eis the average degree of polymerization. The raw materials used in theabove reactions, polyhydroxystyrene (I), diazonaphthoquinone halide(II), poly(styrene-acrylate) resin (III) and novolac resin (IV), arecommercially available or can be synthesized by known methods.

The amine used in preparing the polymers of the present invention ispreferably trialkylamine, and more preferably triethylamine.

The solvent used in preparing the polymers of the present invention maybe selected from the group consisting of tetrahydrofuran, toluene,benzene, methylethylketone and dioxane.

The reaction temperature of the polymerization process used forpreparing the polymers of the present invention is preferably between 50and 80° C.

The present invention also provides an anti-reflective coatingcomposition containing a polymer of the general formula 1, 2 or 3 alonein an organic solvent.

Anti-reflective coating composition of the present invention may alsocomprise one of the polymers of general formula 1, 2 or 3 and a lightabsorbing compound selected from the group consisting of anthracene andits derivatives, fluorenone derivatives, fluorene and its derivatives,fluorenol, xanthone, quinazarin and fluorescein. Examples of suchcompounds are listed in Tables 1a and 1b below:

TABLE 1a

In Table 1a above, R₅, R₆ and R₇ each represent independently hydrogen,a substituted or non-substituted straight or branched C₁-C₅ alkyl group,cycloalkyl, alkoxyalkyl or cycloalkoxyalkyl, and p is an integer.Preferably P has a value of 1˜3.

In Table 1b above, R₈-R₁₅ each represent independently hydrogen,hydroxy, substituted or non-substituted straight or branched C₁-C₅alkyl, cycloalkyl, alkoxyalkyl or cycloalkoxyalkyl, and R₁₆ and R₁₇ eachindependently represent an alkyl group.

The anti-reflective coating composition of the present invention isprepared by dissolving a polymer of general formula 1, 2 or 3 above inan organic solvent, and subsequently adding thereto one or morecompounds selected from the above Tables 1a and 1b.

The organic solvent used for the preparation can be any suitableconventional organic solvent, preferably a solvent selected from thegroup consisting of ethyl 3-ethoxypropionate, methyl3-methoxypropionate, cyclohexanone, propylene glycol andmethyletheracetate.

The amount of the solvent used in preparing the anti-reflective coatingcomposition according to the present invention is preferably200-5000%(w/w) with respect to the weight of the polymer used.

An anti-reflective coating of the present invention can be provided on asemiconductor silicon wafer by filtering a solution of a polymer ofgeneral formula 1, 2 or 3 alone, or a composition containing a polymerof general formula 1, 2 or 3 and one or more of the light-absorbingcompounds set forth in Tables 1a and 1b, subsequently coating thefiltered solution or composition on a wafer that has been prepared inthe conventional manner and “hard-baking” the coating (heating the waferto a temperature of 100-300° C. for 10-1000 seconds) to cross-link theanti-reflective coating polymer.

The polymers comprising the anti-reflective coating of the presentinvention form a cross-linked structure when they are coated on a waferand baked at high temperatures (“hard-baked”) through a reaction whichopens the ring of the diazonaphthoquinone group in said polymers. Thiscross-linked structure allows the polymers of the present invention toform an organic anti-reflective coating material which isspectroscopically stable under conventional photolithographicconditions.

The polymers and compositions of the present invention have proven to beexcellent organic anti-reflective coating materials during the formationof submicro-patterns in photolithographic processes using 248 nm KrF and193 nm ArF lasers. The anti-reflective effect provided in accordancewith the present invention have also been found to be superior whenE-beam, extreme ultraviolet (EUV) light, and ion beam light sources areused instead of an ArF beam.

The invention will be further illustrated by the following examples, butthe invention is not limited to the examples given.

EXAMPLE 1 Synthesis of Copolymer of Polyhydroiystyrene Having aDiazonaphthoqyinonesulfonyl Group

After dissolving completely 49.6 g (0.3 moles) of polyhydroxystyreneresin in a 300 ml round bottomed flask containing 250 g oftetrahydrofuran (THF), 15.2 g (0.15 moles) of triethylamine is added tothe mixture and mixed completely. Into the mixture, 45.1 g (0.15 moles)of diazonaphthoquinone chloride is added slowly and reacted for morethan 24 hours. After the completion of the reaction, the resin isseparated by precipitating it in diethylether and dried under vacuum toobtain a poly(hydroxystyrene-diazonaphthoquinonesulfonylstyrene)copolymer of the present invention wherein 50% of hydroxystyrene monomeris substituted with a diazonaphthoquinonesulfonyl group. The yield is90-95%.

EXAMPLE 2 Synthesis of Copolymer of Polyhydroxy—Methylstyrene Having aDiazonaphthoguinonesulfonyl Group

After dissolving completely 58.8 g (0.33 moles) ofpolyhydroxy-(-methylstyrene resin in a 300 ml round bottomed flaskcontaining 250 g of tetrahydrofuran (THF), 13.45 g (0.132 moles) oftriethylamine is added to the mixture and mixed completely. Into themixture, 39.7 g (0.132 moles) of diazonaphthoquinone chloride is addedslowly and reacted for more than 24 hours. After the completion of thereaction, the resin is separated by precipitating it in diethylether anddried under vacuum to obtain apoly(hydroxy—methylstyrene-diazonaphthoquinonesulfonyl-(-methylstyrene)copolymer of the present invention wherein 40% of thehydroxy—methylstyrene monomer is substituted with adiazonaphthoquinonesulfonyl group. The yield is 90-95%.

EXAMPLE 3 Synthesis of Copolymer ofPoly(Hydroxystyrene-hydroxyethylacrylate) Having aDiazonaphthoguinonesulfonyl Group

After dissolving completely 84.1 g (0.3 moles) ofpoly(hydroxystyrene-hydroxyethylacrylate) resin in a 300 ml roundbottomed flask containing 300 g of tetrahydrofuran (THF), 15.2 g (0.15moles) of triethylamine is added to the mixture and mixed completely.Into the mixture, 45.1 g (0.15 moles) of diazonaphthoquinone chloride isadded slowly and reacted for more than 24 hours. After the completion ofthe reaction, the resin is separated by precipitating it in diethyletherand dried under vacuum to obtain apoly(hydroxystyrene-hydroxyethylacrylate) copolymer of the presentinvention wherein 50% of reactant is substituted with adiazonaphthoquinonesulfonyl group. The yield is 85-90%.

EXAMPLE 4 Synthesis of CopolymerPoly(Hydroxystyrene-hydroxyethylmethacrylate) Having aDiazonaphthoguinonesulfonyl Group

After dissolving completely 88.3 g (0.3 moles) ofpoly(hydroxystyrene-hydroxyethylmethacrylate) resin in a 300 ml roundbottomed flask containing 300 g of tetrahydrofuran (THF), 13.7 g (0.135moles) of triethylamine is added to the mixture and mixed completely.Into the mixture, 40.6 g (0.135 moles) of diazonaphthoquinone chlorideis added slowly and reacted for more than 24 hours. After the completionof the reaction, the resin is separated by precipitating it indiethylether and dried under vacuum to obtain ahydroxystyrene-hydroxyethylnethacrylate resin of the present inventionwherein 45% of the reactant is substituted with adiazonaphthoquinonesulfonyl group. The yield is 90-95%.

EXAMPLE 5 Synthesis of Phenylnovolac Copolymer Having aDiazonaphthoquinonesulfonyl Group

After dissolving completely 63.1 g (0.35 moles) of phenylnovolac resinin a 300 ml round bottomed flask containing 250 g of tetrahydrofuran(THF), 17.7 g (0.175 moles) of triethylamine is added to the mixture andmixed completely. Into the mixture, 52.6 g (0.175 moles) ofdiazonaphthoquinone chloride is added slowly and reacted for more than24 hours. After the completion of the reaction, the resin is separatedby precipitating it in diethylether and dried under vacuum to obtain aphenylnovblac resin of the present invention wherein 50% of the reactantis substituted with a diazonaphthoquinonesulfonyl group. The yield is90-95%.

EXAMPLE 6 Synthesis of Cresolnovolac Copolymer Having aDiazonaphthoquinonesulfonyl Group

After dissolving completely 62.2 g (0.3 moles) of cresolnovolac resin ina 300 ml round bottomed flask containing 250 g of tetrahydrofuran (THF),15.2 g (0.15 moles) of triethylamine is added to the mixture and mixedcompletely. Into the mixture, 45.1 g (0.15 moles) of diazonaphthoquinonechloride is added slowly and reacted for more than 24 hours. After thecompletion of the reaction, the resin is separated by precipitating itin diethylether and dried under vacuum to obtain a cresolnovolac resinof the present invention wherein 50% of the reactant is substituted witha diazonaphthoquinonesulfonyl group. The yield is 90-95%.

EXAMPLE 7 Preparation of Anti-reflective Coating Film

50 mg of a copolymer prepared in accordance with Examples 1 through 6above is mixed with 0.1-30%(w/w) of one of the compounds in Tables 1aand 1b above in about 100 g of propylene glycol methyletheracetate(PGMEA) and the mixture is dissolved completely. The solution isfiltered, coated on a wafer and hard-baked at 100-300° C. for 10-1000seconds. Afterwards, a light-sensitive film is coated on thisanti-reflective film to provide a semiconductor device suitable for finepattern formation in a conventional photolithographic process.

The polymers of the present invention have high solubilities in most ofthe hydrocarbon solvents, but the anti-reflective coating is renderedinsoluble in any solvent after hard-baking. Accordingly, the polymers ofthe present invention are superior for use in a photoresist film and donot exhibit problems such as cutting or footing during the patternformation.

When the polymers of the present invention are used as anti-reflectivecoatings in the submicro-pattern formation process of preparingsemiconductors, the product yield is increased because the eliminationof the CD variation originating from lower layers forms stable 64 M, 256M, 1 G, 4 G, 16 G DRAM submicro-patterns.

What is claimed is:
 1. An anti-reflective coating compositioncomprising: (a) a diazonapthoquinonesulfonyl-substituted polymerselected from the group consisting of: (i) a polyhydroxystyrene polymerof the formula:

 wherein each R is independently hydrogen, a C₁-C₆ alkyl group, hydroxyor hydroxymethyl; and m:n is the mole ratio of 0.1-0.9:0.1-0.9; (ii) apoly(styrene-acrylate) polymer of the formula:

 wherein each R is independently hydrogen, an C₁-C₆ alkyl group, hydroxyor hydroxymethyl; each x is independently an integer from 1 and 5; anda:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9; and (iii)a novolac polymer of the formula:

 wherein each R₁ is independently hydrogen, methyl or hydroxy; and e isthe average degree of polymerization; and (b) one or morelight-absorbing compounds selected from the group consisting ofanthracene and its derivatives, fluorenone derivatives, fluorene and itsderivatives, fluorenol, xanthone, quinazarin and fluorescein.
 2. Theanti-reflective coating composition according to claim 1, wherein saidlight-absorbing compound is anthracene, 9-anthracenemethanol,9-anthracenecarbonitrile, 9-anthracenecarboxylic acid, dithranol,1,2,10-anthracenetriol, anthraflavic acid, 9-anthraldehyde oxime,9-anthraldehyde, 2-amino-7-methyl-5-oxo-5H-benzopyranopyridine-3-carbonitrile, 1-aminoanthraquinone,anthraquinone-2-carboxylic acid, 1,5-dihydroxyanthraquinone, anthrone,9-anthryltrifluoromethylketone, fluorene, 9-fluorene acetic acid,2-fluorene carboxaldehyde, 2-fluorene carboxylic acid, 1-fluorenecarboxylic acid, 4-fluorene carboxylic acid, 9-fluorene carboxylic acid,9-fluorene methanol, fluorenol, xanthone, quinizarin, fluorescein, a9-alkyl anthracene derivative of the formula:

a 9-carboxylic anthracene derivative of the formula:

a 1-carboxyl anthracene derivative of the formula:

a fluorenone derivative of the formula:

a fluorenone derivative of the formula:

a fluorenone derivative of the formula:

or a fluorenone derivative of the formula:

wherein, each of R₅, R₆ and R₇ is independently hydrogen, substituted ornon-substituted straight or branched C₁-C₅ alkyl, cycloalkyl,alkoxyalkyl or cycloalkoxyalkyl; each of R₈-R₁₅ is independentlyhydrogen, hydroxy, substituted or non-substituted straight or branchedC₁-C₅ alkyl, cycloalkyl, alkoxyalkyl or cycloalkoxyalkyl; each of R₁₆and R₁₇ is independently alkyl; and p is an integer.
 3. Ananti-reflective coating composition according to claim 1 wherein thecomposition is used for KrF lithography.
 4. A process of preparing ananti-reflective coating composition which comprises: dissolving adiazonapthoquinonesulfonyl-substituted polymer in 200˜5000%(w/w) of anorganic solvent, wherein the diazonapthoquinonesulfonyl-substitutedpolymer is selected from the group consisting of: (i) apolyhydroxystyrene polymer of the formula:

 wherein each R is independently hydrogen, a C₁-C₆alkyl group, hydroxyor hydroxymethyl; and m:n is the mole ratio of 0.1-0.9:0.1-0.9; (ii) apoly(styrene-acrylate) polymer of the formula:

 wherein each R is independently hydrogen, an C₁-C₆ alkyl group, hydroxyor hydroxymethyl; each x is independently an integer from 1 and 5; anda:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9; and (iii)a novolac polymer of the formula:

 wherein each R₁ is independently hydrogen, methyl or hydroxy; and e isthe average degree of polymerization; and adding to the resultingsolution one or more light-absorbing compounds selected from the groupconsisting of anthracene, 9-anthracenemethanol,9-anthracenecarbonitrile, 9-anthracenecarboxylic acid, dithranol, 1, 2,10-anthracenetriol, anthraflavic acid, 9-anthraldehyde oxime,9-anthraldehyde, 2-amino-7-methyl-5-oxo-5H-benzopyranopyridine-3-carbonitrile,1-aminoanthraquinone, anthraquinone-2-carboxylic acid, 1,5-dihydroxyanthraquinone, anthrone, 9-anthryltrifluoromethylketone,fluorene, 9-fluorene acetic acid, 2-fluorene carboxaldehyde, 2-fluorenecarboxylic acid, 1-fluorene carboxylic acid, 4-fluorene carboxylic acid,9-fluorene carboxylic acid, 9-fluorene methanol, fluorenol, xanthone,quinizarin, fluorescein, a 9-alkyl anthracene derivative of the formula:

a 9-carboxylic anthracene derivative of the formula:

a 1-carboxyl anthracene derivative of the formula:

a fluorenone derivative of the formula:

a fluorenone derivative of the formula:

a fluorenone derivative of the formula:

and a fluorenone derivative of the formula:

wherein, each of R₅, R₆ and R₇ is independently hydrogen, substituted ornon-substituted straight or branched C₁-C₅ alkyl, cycloalkyl,alkoxyalkyl or cycloalkoxyalkyl; each of R₈-R₁₅ is independentlyhydrogen, hydroxy, substituted or non-substituted straight or branchedC₁-C₅ alkyl, cycloalkyl, alkoxyalkyl or cycloalkoxyalkyl; each of R₁₆and R₁₇ is independently alkyl; and p is an integer.
 5. A processaccording to the claim 4 wherein the amount of the light-absorbingcompound is 0.1-40%(w/w).
 6. A process according to claim 4 wherein thesolvent is selected from the group consisting of ethyl3-ethoxypropionate, methyl 3-methoxypropionate, cyclohexanone, propyleneglycol, and methyletheracetate.
 7. An anti-reflective coatingcomprising: a diazonapthoquinonesulfonyl-substituted polymer selectedfrom the group consisting of: (i) a polyhydroxystyrene polymer of theformula:

wherein each R is independently hydrogen, a C₁-C₆ alkyl group, hydroxyor hydroxymethyl; and m:n is the mole ratio of 0.1-0.9:0.1-0.9; (ii) apoly(styrene-acrylate) polymer of the formula:

wherein each R is independently hydrogen, an C₁-C₆ alkyl group, hydroxyor hydroxymethyl; each x is independently an integer from 1 and 5; anda:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9; and (iii)a novolac polymer of the formula:

wherein each R₁ is independently hydrogen, methyl or hydroxy; and e isthe average degree of polymerization.
 8. An anti-reflective coatingaccording to the claim 7 suitable for use in ArF photolithography.
 9. Aprocess of forming an anti-reflective coating comprising the steps of:dissolving a diazonapthoquinonesulfonyl-substituted polymer in a solventto form a solution, wherein the diazonapthoquinonesulfonyl-substitutedpolymer selected from the group consisting of: (i) a polyhydroxystyrenepolymer of the formula:

 wherein each R is independently hydrogen, a C₁-C₆ alkyl group, hydroxyor hydroxymethyl; and m:n is the mole ratio of 0.1-0.9:0.1-0.9; (ii) apoly(styrene-acrylate) polymer of the formula:

 wherein each R is independently hydrogen, an C₁-C₆ alkyl group, hydroxyor hydroxymethyl; each x is independently an integer from 1 and 5; anda:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9; and (iii)a novolac polymer of the formula:

 wherein each R₁ is independently hydrogen, methyl or hydroxy; and e isthe average degree of polymerization; coating said solution on a siliconwafer; and hard-baking said wafer at 100-300° C. for 10-1000 seconds.10. The process of forming an anti-reflective coating according to claim9, wherein the solution further comprises: one or more of thelight-absorbing compounds selected from the group consisting ofanthracene, 9-anthracenemethanol, 9-anthracenecarbonitrile,9-anthracenecarboxylic acid, dithranol, 1,2,10-anthracenetriol,anthraflavic acid, 9-anthraldehyde oxime, 9-anthraldehyde,2-amino-7-methyl-5-oxo-5H-benzopyrano pyridine-3-carbonitrile,1-aminoanthraquinone, anthraquinone-2-carboxylic acid, 1,5-dihydroxyanthraquinone, anthrone, 9-anthryltrifluoromethylketone,fluorene, 9-fluorene acetic acid, 2-fluorene carboxaldehyde, 2-fluorenecarboxylic acid, 1-fluorene carboxylic acid, 4-fluorene carboxylic acid,9-fluorene carboxylic acid, 9-fluorene methanol, fluorenol, xanthone,quinizarin, fluorescein, a 9-alkyl anthracene derivative of the formula:

a 9-carboxylic anthracene derivative of the formula:

a 1-carboxyl anthracene derivative of the formula:

a fluorenone derivative of the formula:

a fluorenone derivative of the formula:

a fluorenone derivative of the formula:

and a fluorenone derivative of the formula:

wherein, each of R₅, R₆ and R₇ is independently hydrogen, substituted ornon-substituted straight or branched C₁-C₅ alkyl, cycloalkyl,alkoxyalkyl or cycloalkoxyalkyl; each of R₈ -R₁₅ is independentlyhydrogen, hydroxy, substituted or non-substituted straight or branchedC₁-C₅ alkyl, cycloalkyl, alkoxyalkyl or cycloalkoxyalkyl; each of R₁₆and R₁₇ is independently alkyl; and p is an integer.
 11. A semiconductordevice comprising an anti-reflective coating containing adiazonapthoquinonesulfonyl-substituted polymer selected from the groupconsisting of: (a) a polyhydroxystyrene polymer of the formula:

wherein each R is independently hydrogen, a C₁-C₆ alkyl group, hydroxyor hydroxymethyl; and m:n is the mole ratio of 0.1-0.9:0.1-0.9; (ii) apoly(styrene-acrylate) polymer of the formula:

wherein each R is independently hydrogen, an C₁-C₆ alkyl group, hydroxyor hydroxymethyl; each x is independently an integer from 1 and 5; anda:b:c:d is the mole ratio of 0.1-0.9:0.1-0.9:0.1-0.9:0.1-0.9; and (iii)a novolac polymer of the formula:

wherein each R₁ is independently hydrogen, methyl or hydroxy; and e isthe average degree of polymerization.